The following information is provided for guidance only. The rate of heating, cooling and soaking times will vary due to the shape and size of each component and other external factors.
Annealing
Heat the M2 high-speed steel to 850 - 900°C. Hold at temperature for at least two hours or one hour per 25 mm of thickness. Furnace cool slowly. The maximum hardness should be 248 Brinell.
Stress relieving
Stress relieving M2 is recommended after machining or grinding and before hardening to minimise the chance of distortion. Heat the component to 600 - 700°C and soak well (for approximately two hours), then cool in air.
Hardening
Pre heat the M2 in two steps; 450 - 500°C then 850 - 900°C. Then continue heating to the final hardening temperature of 1200 - 1250°C. Do not leave the steel too long at the hardening temperature. Quench in warm oil or brine to about 500°C then air cool down to room temperature.
Tempering
Heat the M2 to the required tempering temperature, hold at temperature for at least two hours or one hour per 25 mm of thickness. Double tempering is recommended.
Additional Information:
Product Details:
Minimum Order Quantity | 100 Kilogram |
Application | Construction |
Size | M35 |
Shape | Square Bar |
Material Grade | HSS |
Single Piece Length | 3 meter, 6 meter |
Thickness/Diameter | 3-4 inch |
The well balance properties of M35 means it is used in a wide range of cutting tools where demands for hot hardness are moderate, such as twist drills, reamers, broaching tools, milling tools, taps and metal saws. M35 is also suitable for cold work applications such as tools for punching, forming and pressing. If you are looking for superior red-hardness then consider M42 high speed steel.
Specifications:
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IM 35 | 0.92 | 4.1 | 5 | 1.9 | 6.4 | 4.8 | S 705 | M41 | BM 35 | XT90W6Co Mo5Cr4V2 | SKH-55 | S 6-5-2-5 (1.3243) |
Additional Information:
Product Details:
Minimum Order Quantity | 100 Kilogram |
Shape | Round |
Single Piece Length | 3 meter, 6 meter |
Size | M42 |
Application | Construction |
Thickness/Diameter | 3-4 inch |
The well balance properties of M42 means it is used in a wide range of cutting tools where demands for hot hardness are moderate, such as twist drills, reamers, broaching tools, milling tools, taps and metal saws. M2 is also suitable for cold work applications such as tools for punching, forming and pressing. If you are looking for superior red-hardness then consider M42 high speed steel.
Specifications:
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IM 42 | 1.1 | 3.9 | 9.2 | 1.2 | 1.4 | 7.8 | S 500 | M42 | BM 42 | XT110Mo10 Co8Cr4W2 | SKH-59 | S 2-10-1-8 (1.3247) |
Additional Information:
Product Details:
Minimum Order Quantity | 1050 Kilogram |
Shape | Square |
Type | Bar |
Material | Alloy Steel |
Application | Pharmaceutical / Chemical Industry, Oil & Gas Industry, Construction, Automobile Industry |
For mordern industrial production, particularly mass production, machining is one of the most important shaping and forming processes. Almost all tools employed for this purpose are made from high speed steels. In recent times, the use of high speed steels has also gained increasing importance for chipless shaping, eg. for extrusion, blanking and punching tools. With regard to chemical composition, distinction made between W-, Mo- and W-Mo alloyed steel grades which, depending on the dominant stress they will be exposed to contain different amounts of carbon, vanadium and cobalt.
The characteristic properties of all high speed steel grades includes:
Influence of alloying elements on the properties:
Carbon | : forms carbides, increases wear resistance, is responsible for the basic matrix hardness. |
---|---|
Tungsten and molybdenum | : improve red hardness, retention of hardness and high temperature strength of the matrix, form special carbides of great hardness. |
Vanadium | : forms special carbides of supreme hardness, increases high temperature wear resistance, retention of hardness and high temperature strength of the matrix. |
Chromium | : promotes depth hardening, produces readily soluble carbides. |
Cobalt | : improves red hardness and retention of hardness of the matrix. |
Additional Information:
Product Details:
Minimum Order Quantity | 100 Kilogram |
Material Grade | HSS |
Single Piece Length | >36 meter |
Application | Construction, Manufacturing |
Thickness/Diameter | >4 inch |
T42 high-speed steel is a tungsten-molybdenum tool steel. M35 is characterised by well-balanced toughness, wear resistance and red hardness properties. AISI T42 high-speed steel has largely replaced T1 in most applications due to its superior properties and advantageous pricing. T42 is medium-alloyed and is a good all-round performer with good machinability, in this respect it is superior to the high alloyed cold work steels.
Specifications:
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IM 35 | 0.92 | 4.1 | 5 | 1.9 | 6.4 | 4.8 | S 705 | M41 | BM 35 | XT90W6Co Mo5Cr4V2 | SKH-55 | S 6-5-2-5 (1.3243) |
Additional Information:
Product Details:
Application | Industrial |
Shape | Squar |
Material | High Speed Steel Square Bar T15 |
Material Grade | High Speed Steel Square Bar T15 |
Single Piece Length | 18 meter, 3 meter, 6 meter, >36 meter, 36 meter |
Modal Number | High Speed Steel Square Bar T15 |
Technique | High Speed Steel Square Bar T15 |
Standards | T15 |
Usage/Application | Household Repair |
Grades Din | T15 |
Condition | New |
We excel in offering a remarkable range of High Speed Steel Squar Bar T15 to our valuable clients.Manufactured using quality assured material, the standard diameter of these bars is 3.17 mm to 350 mm. Besides, we offer these bars in different thickness and dimensions so as to meet the diverse requirements of our clients. These products are widely acclaimed in the market for their durability, corrosion-resistance and accurate dimension.
Clients can avail these round bars in different variety that are mentioned below:
Specifications:
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IT1 | 0.75 | 4.1 | - | 1.1 | 18 | - | S 200 | T1 | BT1 | XT72W18 Cr4V1 | SKH-2 | S 18-0-1 (1.3355) |
Product Details:
Shape | Squar |
Material | High Speed Steel Square Bar T42 |
Material Grade | T42 |
Single Piece Length | 36 meter |
Modal Number | T42 |
Technique | Automobile Industry,Construction,Pharmaceutical / Chemical Industry,Oil & Gas Industry |
Condition | New |
For modern industrial production, in particular mass production, machining is one of the most important shaping and forming processes. Almost all tools employed for this purpose are made from high speed steels. The characteristic properties of all high speed steels grades include.
Influence of alloying elements on the steel properties:
Specifications:
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IT42 | 1.25 | 4 | 3.6 | 3.2 | 9.3 | 10 | S 700 | - | BT 42 | XT125WCo10 CrMo4V3 | SKH-57 | S10-4-3-10 (1.3207) |
Product Details:
Application | Industrial |
Material | High Speed Steel Square Bar T1 |
Material Grade | T1 |
Modal Number | High Speed Steel Square Bar T1 |
Standards | High Speed Steel Square Bar T1 |
Condition | New |
We excel in offering a remarkable range of High Speed Steel Squar Bar T1 to our valuable clients.Manufactured using quality assured material, the standard diameter of these bars is 3.17 mm to 350 mm. Besides, we offer these bars in different thickness and dimensions so as to meet the diverse requirements of our clients. These products are widely acclaimed in the market for their durability, corrosion-resistance and accurate dimension.
Clients can avail these round bars in different variety that are mentioned below:
Specifications:
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IT1 | 0.75 | 4.1 | - | 1.1 | 18 | - | S 200 | T1 | BT1 | XT72W18 Cr4V1 | SKH-2 | S 18-0-1 (1.3355) |
Product Details:
Minimum Order Quantity | 100 Kilogram |
Size | M3 |
Shape | Square |
Material Grade | HSS |
Single Piece Length | 3 meter, 6 meter |
Application | Construction |
Thickness/Diameter | 3-4 inch |
Type | Bar |
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IM 3 CL2 | 1.2 | 4.3 | 5.1 | 3.3 | 6.4 | - | S 607 | M3 CL2 | BM 4 | - | SKH-53 | S 6-5-3 (1.3344) |
Additional Information:
Product Details:
Minimum Order Quantity | 100 Kilogram |
Shape | Square |
Material | Stainless steel |
Application | Pharmaceutical / Chemical Industry, Oil & Gas Industry, Automobile Industry, Construction |
Annealing:
Heat the M2 high-speed steel to 850 - 900°C. Hold at temperature for at least two hours or one hour per 25 mm of thickness. Furnace cool slowly. The maximum hardness should be 248 Brinell.
Stress relieving:
Stress relieving M2 is recommended after machining or grinding and before hardening to minimise the chance of distortion. Heat the component to 600 - 700°C and soak well (for approximately two hours), then cool in air.
Hardening:
Pre heat the M2 in two steps; 450 - 500°C then 850 - 900°C. Then continue heating to the final hardening temperature of 1200 - 1250°C. Do not leave the steel too long at the hardening temperature. Quench in warm oil or brine to about 500°C then air cool down to room temperature.
Tempering:
Heat the M2 to the required tempering temperature, hold at temperature for at least two hours or one hour per 25 mm of thickness. Double tempering is recommended.
Specifications:
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IM 2 | 0.9 | 4.1 | 5 | 1.8 | 6.4 | - | S 600 | M2 | BM 2 | XT87W6Mo5 Cr4V2 | SKH-51 | S 6-5-2 (1.3343) |
Additional Information:
Product Details:
Minimum Order Quantity | 100 Kilogram |
Type | Square Bar |
Material | Stainless steel |
Application | Construction, Oil & Gas Industry, Automobile Industry, Pharmaceutical / Chemical Industry |
For mordern industrial production, particularly mass production, machining is one of the most important shaping and forming processes. Almost all tools employed for this purpose are made from high speed steels. In recent times, the use of high speed steels has also gained increasing importance for chipless shaping, eg. for extrusion, blanking and punching tools. With regard to chemical composition, distinction made between W-, Mo- and W-Mo alloyed steel grades which, depending on the dominant stress they will be exposed to contain different amounts of carbon, vanadium and cobalt.
The characteristic properties of all high speed steel grades includes:
Influence of alloying elements on the properties:
Carbon | : forms carbides, increases wear resistance, is responsible for the basic matrix hardness. |
---|---|
Tungsten and molybdenum | : improve red hardness, retention of hardness and high temperature strength of the matrix, form special carbides of great hardness. |
Vanadium | : forms special carbides of supreme hardness, increases high temperature wear resistance, retention of hardness and high temperature strength of the matrix. |
Chromium | : promotes depth hardening, produces readily soluble carbides. |
Cobalt | : improves red hardness and retention of hardness of the matrix. |
Powmax Grade | Chemical Composition (Average Value in %) Standard | Standard | ||||||||||
C | Cr | Mo | V | W | Co | Bohler | AISI | BS | IS | JIS | DIN | |
IM 7 | 0.97 | 3 | 8.2 | 1.75 | 1.4 | - | S 400 | M7 | - | - | SKH-58 | S 2-9-2 (1.3348) |